Recently, through a friend, I learned of a project on the Kickstarter site that piqued my interest.  It had to do with a new rapid prototyping system and Michael Joyce, the guy who was seeking funding on Kickstarter, for the B9Creator, had developed a system similar in some ways to existing technology, yet different enough, and simple enough that he was offering the complete machine for a funding pledge of something close to 1/10th the cost of the other similar machines.  My respect grew for this inventor when I learned that he was creating the project as a completely open source project such that other people could understand, and perhaps improve the system over time.  Mr. Joyce didn’t necessarily develop this system specifically for the jewelry industry, but as CAD-CAM (Computer Aided Design-Computer Aided Manufacturing)  is currently becoming more the standard rather than the exception in contemporary jewelry design, his timing couldn’t have been more spot on for the industry.  The funding for his project attests to his timliness and the interest his project has created.

Other people had already posed the question to Mr. Joyce, “Does this system produce a ‘castable’ product?”  Joyce was pretty sure he knew the answer to that but hadn’t yet acquired third-party verification…enter Gary Dawson Designs!

Here is the entire text and photos of the short research project I created and executed for him.  Note that this test casting was done with some very early test peices of resin and are not at all representative of the resolution that the B9C can now achieve.  In fact, these pieces were chosen for texture.


Initial Assessment of the B9C System for Jewelry Prototyping   By Gary Dawson


Although rapid prototyping technology has become more accessible with the advances inherent in contemporary technological research, leading edge technology still represents a major investment for any manufacturer and is out of reach for some.    If the jewelry industry continues to fragment as noted by this researcher (“Paradigm shift in Jewelry Manufacturing and Market Structure:  An Examination of Contemporary Small Shop Jewelry Production-Design to Manufacture to Retail” Proceedings of the Santa Fe Symposium of Jewelry Manufacturing Technology, 2010) funding of advanced technology may continue to be problematic.  A first look at the B9Creator system of Rapid Prototyping may be indicative of a trend toward more affordable leading edge RP systems with the possible net result of a more rapid adoption of advanced RP technology by the jewelry industry as a whole.



This project was designed as a preliminary test of burnout characteristics of the resin used in the B9C RP-DLP system.



Three sections of cured resin were chosen for their texture in hopes of evaluating possible ash residue and potential problems created by thermal expansion characteristics of the resin during ramp-up within the burn out cycle.  One piece of textured resin was invested in each of two flasks using Ransom & Randolph Ultra-Vest.  Instructions supplied with the investment were followed for mixing and burnout.  One section of cured resin was placed directly on the kiln floor for the purpose of direct observation of ash residue.  The kiln was observed at the end of the burnout cycle and both flasks were cast in Sterling Silver using a horizontal centrifugal.  Melt was accomplished by Hydrogen-Oxygen flame.  If the kiln floor piece had displayed any amount of ash residue, and/or the first casting showed any signs of residue contamination I had planned to use a protocol established by another researcher of using compressed air to clear the mold cavity prior to casting the second flask.  However based on my observation of the kiln floor and the first flask casting results, I felt no need to use this protocol.



  • Upon completion of burnout the kiln floor where the single piece of cured resin was placed was observed to have no ash residue.
  • Both flasks containing cured resin cast normally and seemed to have normal resolution of cast surfaces in all cases which leads to an initial indication of no interior mold degradation due to thermal expansion of the resin during ramp-up in the burnout cycle.


Figure 1:  Texture on sprued resin.

Texture on Sprued Resin segment

Figure 2:  Texture on sprued resin.

Depicting texture on second sprued resin piece

Figure 3:  Interior of kiln prior to initiation of burnout.

Flasks in kiln with resin segment placement on kiln floor

Figure 4:  Interior of kiln after burnout cycle complete.

Interior of kiln after burnout...this picture isn't very clear but there was no evidence of ash residue on the kiln floor at all!

Figure 5:  Cast pieces after pickle, prior to magnetic pin tumbling

rough casting of resin pieces, oxide layer removed with acid bath

Figure 6:  Cast pieces after magnetic pin tumbling.

Same cast pieces after magnetic pin tumbling. This brings out the detail of the casting.



If getting to know interesting people and what they’re up to intrigues you, you might check out Mr. Joyce’s other projects.  .


I’m honored to have been able to contribute in some small way to one of this fellow’s projects!!!


  1. Thank you for taking the time to do this!!

    Comment by Mike Joyce | June 5, 2012

  2. Thank you so much for doing this. I am a first year jewellery design student in Toronto, and have been waiting for someone to test the resins in a jewellery setting. Not only did they exceed my expectations, it worked so well I’m putting this printer at the top of my “To Buy” list for my shop. Thanks again, and i’m a huge fan of your designs!

    Comment by Trevor V. | June 5, 2012

  3. Hey Trevor! It was indeed my pleasure to work with Mike on this. His RP machine may truly represent a huge leap forward for small shops looking to use advancing technology. Best of luck in your jewelry career. It has been a good life for me.
    Best Regards,

    Comment by Gary | June 5, 2012

  4. My pleasure, Mike. Thanks for allowing me the opportunity to participate!

    Comment by Gary | June 5, 2012

  5. Thank you for providing the insight on the Lost Wax casting! This is extremely useful!

    Comment by Yongkiat Karnchanapayap | June 6, 2012

  6. Thanks for putting the time and effort into testing the resin for lost wax casting. Really looking forward to seeing the creations that result from combining these two techniques

    Comment by Jamie | June 7, 2012

  7. Thanks for the experiment Gary. In my opinion this is what it is all about and you have convinced me it is the solution I have been working towards for some time. Thanks again for your efforts…

    Comment by John Grimes | July 5, 2012

  8. This project has come so far this past year! How exciting for all of you involved. It seems to me there are no limits holding you back Mr Dawson! (and Mr Joyce and Mr Dickman)

    Comment by Alysia | June 11, 2013

RSS feed for comments on this post. TrackBack URL

Please leave a comment

Copyright © 2015 Gary Dawson Designs. All rights reserved.